Polyamideimides (PAI) has a very high mechanical strength and hardness at low temperatures and under very high. Polyamideimides (PAI) have stability temperature of the mold and a glass transition temperature (+ 280 ° C).
The PAI polymer sheets will not change its properties even at the highest possible operating temperature, and the Polyamideimide parts will work flawlessly even under excessive heat. and we can produce the series of high-end Engineering Plastic,such as PEEK/PAI/PEI/PI/PVD/FPPS.
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
| Impact strength (Charpy) | 81 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Shore hardness | 85 | - | D scale | DIN EN ISO 868 |
| Compression strength | 12/32/90 | MPa | 1% / 2% / 5% | EN ISO 604 |
Modulus of elasticity
(tensile test) | 3600 | MPa | 1 mm/min | DIN EN ISO 527-2 |
| Tensile strength at break | 122 | MPa | 5mm/min | DIN EN ISO 527-2 |
Modulus of elasticity
(flexural test) | 3600 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Elongation at break | 8 | % | 5mm/min | DIN EN ISO 527-2 |
| Flexural strength | 173 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Ball indentation hardness | 221 | MPa | | ISO 2039-1 |
Application:
PAI products are suitable for many applications such as gears, rollers, plasma chamber hardware, and contact holders. In addition, Torlon can be processed into chip holders and sockets, sliding strips in aerospace, insulation bodies in electrical engineering, slide bushings in hydraulic systems, and sipes in compressors.